Properties of concrete are influenced by many factors mainly due to mix proportion of cement, sand, aggregates and water. Ratio of these materials control the various concrete properties which are discussed below.
Concrete is known by its grade which is designated as M15, M20 etc. in which letter M refers to concrete mix and number 15, 20 denotes the specified compressive strength (fck) of 150mm cube at 28 days, expressed in N/mm 2 . Thus, concrete is known by its compressive strength. M20 and M25 are the most common grades of concrete, and higher grades of concrete should be used for severe, very severe and extreme environments.
Like load, the strength of the concrete is also a quality which varies considerably for the same concrete mix. Therefore, a single representative value, known as characteristic strength is used. Also Read: Compressive strength of concrete cubes
It is defined as the value of the strength below which not more then 5% of the test results are expected to fall (i.e. there is 95% probability of achieving this value only 5% of not achieving the same)
The characteristic strength of concrete in flexural member is taken as 0.67 times the strength of concrete cube.
The strength to be taken for the purpose of design is known is known as design strength and is given by Design strength (fd) = characteristic strength/ partial safety factor for material strength The value of partial safety factor depends upon the type of material and upon the type of limit state. According to IS code, partial safety factor is taken as 1.5 for concrete and 1.15 for steel. Design strength of concrete in member = 0.45fck
The estimate of flexural tensile strength or the modulus of rupture or the cracking strength of concrete from cube compressive strength is obtained by the relations fcr = 0.7 fck N/mm 2 . The tensile strength of concrete in direct tension is obtained experimentally by split cylinder. It varies between 1/8 to 1/12 of cube compressive strength. Read More on Tensile strength of concrete
Creep is defined as the plastic deformation under sustained load. Creep strain depends primarily on the duration of sustained loading. According to the code, the value of the ultimate creep coefficient is taken as 1.6 at 28 days of loading. Read More on Concrete Creep
The property of diminishing in volume during the process of drying and hardening is termed Shrinkage. It depends mainly on the duration of exposure. If this strain is prevented, it produces tensile stress in the concrete and hence concrete develops cracks.
Short term modular ratio is the modulus of elasticity of steel to the modulus of elasticity of concrete. Short term modular ratio = Es / Ec Es = modulus of elasticity of steel (2 x 10 5 N/mm 2 ) Ec = modulus of elasticity of concrete (5000 x SQRT(fck) N/mm 2 ) As the modulus of elasticity of concrete changes with time, age at loading etc the modular ratio also changes accordingly. Taking into account the effects of creep and shrinkage partially IS code gives the following expression for the long term modular ratio. Long term modular ratio (m) = 280/ (3fcbc) Where, fcbc = permissible compressive stress due to bending in concrete in N/mm 2 .
Poisson’s ratio varies between 0.1 for high strength concrete and 0.2 for weak mixes. It is normally taken as 0.15 for strength design and 0.2 for serviceability criteria.
Durability of concrete is its ability to resist its disintegration and decay. One of the chief characteristics influencing durability of concrete is its permeability to increase of water and other potentially deleterious materials. The desired low permeability in concrete is achieved by having adequate cement, sufficient low water/cement ratio, by ensuring full compaction of concrete and by adequate curing. Read More on Concrete Durability
The unit weight of concrete depends on percentage of reinforcement, type of aggregate, amount of voids and varies from 23 to 26 kN/m 2 . The unit weight of plain and reinforced concrete as specified by IS:456 are 24 and 25 KN/m 3 respectively.